We have our own profits team, layout crew, technical team, QC team and package team. Now we have strict top quality handle procedures for each procedure. Also, all of our workers are experienced in printing industry for 2019 High quality China Barium Ferrite Core Magnets for Speaker, Created items with brand worth. We attend seriously to produce and behave with integrity, and from the favor of buyers in your house and abroad from the xxx industry. We have our own profits team, layout crew, technical team, QC team and package team. Now we have strict top quality handle procedures for each procedure. Also, all of our workers are experienced in printing industry for China Ferrite Magnet Speaker, Ferrite Magnet, Our objects have national accreditation requirements for qualified, high quality products and solutions, affordable value, was welcomed by people today all over the world. Our goods will continue to enhance within the order and look forward to cooperation with you, Need to any of those goods be of interest to you, be sure to letus know. We've been gonna be content to offer you a quotation up on receipt of your detailed needs. Introduction: Hard ferrites based on barium ferrite and strontium powders (chemical formula BaO • 6Fe2O3 and SrO • 6Fe2O3) manufactured. They consist of oxidized metals, thus included in the ceramic materials group. They consist of approx. 90% iron oxide (Fe2O3) and 10% alkaline earth oxide (BaO or SrO) – raw materials which are plentiful and inexpensive. They divide into isotropic and anisotropic, the particles of the latter are aligned in a single direction which obtaining better magnetic characteristics. Isotropic magnets are shaped by compressing while anisotropic magnets are compressed within a magnetic field. This provides the magnet with a preferential direction and triples its energy density. Advantage: As is typical of oxide ceramics, hard ferrite magnets display relatively resistant behavior towards moisture, solvents, alkaline solutions, weak acids, salts, lubricants and gas pollutants. Generally, hard ferrite magnets can therefore be used without additional corrosion protection. Feature: Due to their great hardness (6-7 Mohs), Ferrite magnets are brittle and sensitive to knocks or bending. During processing, they have to be machined with diamond tools. Operating temperatures with ferrite magnets are generally between –40ºC and 250ºC. Application: Different shapes are used in utomotive engineering, such as automation and measurement control. Other applications such as Automobile electrical machinery (wipers, sit chair motor), Teaching, Door absorber, Magnetic bike and massage chair, etc. Today, hard ferrites represent the largest proportion of permanent magnets produced. In contrast to AlNiCo magnets, hard ferrites are characterized by flux densities but high coercive field strengths. This results in the generally flat shape of the materials. Barium ferrite and strontium ferrite are differentiated depending on the starting material. All stated values were determined using standard samples according IEC 60404-5. The following specifications serve as reference values and may differ. Sintered Ferrite Magnet Physical Properties Grade Remanence Rev. Temp.   Coeff. Of Br Coercive Force Intrinsic Coercive Force Rev. Temp.-Coeff. Of Hcj Max. Energy Product Max. Operating Temperature Density Br (KGs) Hcb (KOe) Hcj (KOe) (BH)max. (MGOe) g/cm³ Y10T 2.0-2.35 -0.20 1.57-2.01 2.64-3.52 +0.30 0.8-1.2 250℃ 4.95 Y20 3.2-3.8 -0.20 1.70-2.38 1.76-2.45 +0.30 2.3-2.8 250℃ 4.95 Y22H 3.1-3.6 -0.20 2.77-3.14 3.52-4.02 +0.30 2.5-3.2 250℃ 4.95 Y23 3.2-3.7 -0.20 2.14-2.38 2.39-2.89 +0.30 2.5-3.2 250℃ 4.95 Y25 3.6-4.0 -0.20 1.70-2.14 1.76-2.51 +0.30 2.8-3.5 250℃ 4.95 Y26H 3.6-3.9 -0.20 2.77-3.14 2.83-3.21 +0.30 2.9-3.5 250℃ 4.95 Y27H 3.7-4.0 -0.20 2.58-3.14 2.64-3.21 +0.30 3.1-3.7 250℃ 4.95 Y28 3.7-4.0 -0.20 2.20-2.64 2.26-2.77 +0.30 3.3-3.8 250℃ 4.95 Y30 3.7-4.0 -0.20 2.20-2.64 2.64-2.77 +0.30 3.3-3.8 250℃ 4.95 Y30H-1 3.8-4.0 -0.20 2.89-3.46 2.95-3.65 +0.30 3.4-4.1 250℃ 4.95 Y30BH 3.8-3.9 -0.20 2.80-2.95 2.90-3.08 +0.30 3.4-3.7 250℃ 4.95 Y30-1 3.6-4.0 -0.20 1.70-2.14 1.76-2.51 +0.30 2.8-3.5 250℃ 4.95 Y30BH-1 3.8-4.0 -0.20 2.89-3.46 2.95-3.65 +0.30 3.4-4.0 250℃ 4.95 Y30H-2 3.95-4.15 -0.20 3.46-3.77 3.90-4.21 +0.30 3.5-4.0 250℃ 4.95 Y20-2 3.95-4.15 -0.20 3.46-3.77 3.90-4.21 +0.30 3.5-4.0 250℃ 4.95 Y32 4.0-4.2 -0.20 2.01-2.38 2.07-2.45 +0.30 3.8-4.2 250℃ 4.95 Y33 4.1-4.3 -0.20 2.77-3.14 2.83-3.21 +0.30 4.0-4.4 250℃ 4.95 Y35 4.0-4.1 -0.20 2.20-2.45 2.26-2.51 +0.30 3.8-4.0 250℃ 4.95 Note: · We remain the same as above unless specified from customer. Curie temperature and temperature coefficient are for reference only, not as a basis for decision. · The maximum working temperature of magnet is changeable due to ratio of length and diameter and environment factors.